Sopormetal (Perak Las) Fosilver 5 Flat
Rp1.157.000
- Kondisi: Baru
- Min. Pemesanan: 1 Buah
- Etalase: Sopormetal
Standards:
ISO 17672: CuP 281
(EN 1044: CP 104)
(DIN 8513: L-Ag5P)
AWS A5.8M7A5.8: BCuP-3
Chemical Composition:
% Ag : 5,0
% Cu : Rem.
% P : 6,0
Physical and mechanical characteristics:
Melting range (C): 645 815
Working temperature (C): 710
Tensile strength (N/mm2): 250
Elongation (%): 8
Density (g/cm3): 8,2
Applications:
FoSilver 5 has been developed primarily for use in copper, however, its application has been extended to other non-ferrous copper alloys. This alloy is commonly used in refrigeration, air conditioning, electrical conductors, pipes for hot and cold water and pre-fabricated houses.
Particular characteristics:
Its a copper-phosphorus alloy with intermediate percentage of silver with good flow properties, ductility and self-fluxing in copper. It is not advisable its use in nickel alloys and iron-based alloys, under penalty of having formation of brittle compunds at the interface of the joint, giving less good properties. Similary, it is not advisable to use this alloy in sulfurous environments.
Delivery forms:
Rods 1mm, 1.5mm, 2mm, 3mm x 500mm and wire.
Other delivery forms upon request.
Heat sources:
Oxy-acetylene torch, oven, high frequency induction,TIG.
ISO 17672: CuP 281
(EN 1044: CP 104)
(DIN 8513: L-Ag5P)
AWS A5.8M7A5.8: BCuP-3
Chemical Composition:
% Ag : 5,0
% Cu : Rem.
% P : 6,0
Physical and mechanical characteristics:
Melting range (C): 645 815
Working temperature (C): 710
Tensile strength (N/mm2): 250
Elongation (%): 8
Density (g/cm3): 8,2
Applications:
FoSilver 5 has been developed primarily for use in copper, however, its application has been extended to other non-ferrous copper alloys. This alloy is commonly used in refrigeration, air conditioning, electrical conductors, pipes for hot and cold water and pre-fabricated houses.
Particular characteristics:
Its a copper-phosphorus alloy with intermediate percentage of silver with good flow properties, ductility and self-fluxing in copper. It is not advisable its use in nickel alloys and iron-based alloys, under penalty of having formation of brittle compunds at the interface of the joint, giving less good properties. Similary, it is not advisable to use this alloy in sulfurous environments.
Delivery forms:
Rods 1mm, 1.5mm, 2mm, 3mm x 500mm and wire.
Other delivery forms upon request.
Heat sources:
Oxy-acetylene torch, oven, high frequency induction,TIG.