FusForceTM PAHT-CF 500 gr
Product Description
FusForceTM PAHT-CF is specially developed for FDM 3D printing process, and its substrate material is high temperature nylon, which has low density, low moisture absorption, high strength, high abrasion resistance, excellent chemical resistance and high heat resistance. It also has good dimensional stability, no warpage and no shrinkage during the printing process, and can be used with FusFreeTM S-PAHT Quick-Remove Support material to solve the problem of poor molding effect on the support surface of complex models.
Printing Tips：
1、The wear resistance of copper nozzle is poor. It is recommended to use stainless steel or hardened steel nozzle to print, which can effectively improve the printing quality.
2、Please put filament into a dry box, which can effectively reduce the oozing, rough surface and so on.
Specimens printed under the following conditions: Nozzle temp 320℃, Bed temp 80℃, Print speed 45mm/s, Infill 100%, Infill angle ±45° Post-processing: 100°C Annealing 8 hours
Nozzle Temperature
300-320 °C
Recommended Nozzle Diameter 0.4-1.0 mm
Recommended build surface treatment PEI Film or Coating with PVP glue
Build plate temperature 70-90 °C
Raft separation distance 0.12-0.16 mm
Cooling fan speed Off
Print speed 30-90 mm/s
Retraction distance 1-3 mm
Retraction speed 1800-3600 mm/min
Product Description
FusForceTM PAHT-CF is specially developed for FDM 3D printing process, and its substrate material is high temperature nylon, which has low density, low moisture absorption, high strength, high abrasion resistance, excellent chemical resistance and high heat resistance. It also has good dimensional stability, no warpage and no shrinkage during the printing process, and can be used with FusFreeTM S-PAHT Quick-Remove Support material to solve the problem of poor molding effect on the support surface of complex models.
Printing Tips：
1、The wear resistance of copper nozzle is poor. It is recommended to use stainless steel or hardened steel nozzle to print, which can effectively improve the printing quality.
2、Please put filament into a dry box, which can effectively reduce the oozing, rough surface and so on.
Specimens printed under the following conditions: Nozzle temp 320℃, Bed temp 80℃, Print speed 45mm/s, Infill 100%, Infill angle ±45° Post-processing: 100°C Annealing 8 hours
Nozzle Temperature
300-320 °C
Recommended Nozzle Diameter 0.4-1.0 mm
Recommended build surface treatment PEI Film or Coating with PVP glue
Build plate temperature 70-90 °C
Raft separation distance 0.12-0.16 mm
Cooling fan speed Off
Print speed 30-90 mm/s
Retraction distance 1-3 mm
Retraction speed 1800-3600 mm/min